Ductile stainless steel mesh

Stainless steel mesh is generally not corroded, but nothing is absolute. Corrosion fracture of stainless steel mesh is a corrosive fracture that occurs under the simultaneous action of stress and corrosive environment. Generally speaking, stainless steel mesh will accelerate the rate of corrosion damage in the corrosive environment under external stress.

The simplest case is the result of the superposition of these two factors. In a particular corrosive environment, when the metal material is not stressed, the corrosion damage is minimal, and when subjected to a certain stress, although the stress is sometimes much lower than The strength limit of the stainless steel mesh itself, even after a period of time, even the stainless steel mesh with good ductility will break.

Such damage is often without warning, and the damage caused is very serious and often catastrophic. There are roughly three necessary conditions for stress corrosion fracture. The special environment must be affected by tensile force; the stainless steel mesh itself is of poor quality.

Classified by variety: stainless steel plain weave mesh. Stainless steel twill mesh. Stainless steel bamboo pattern net. Five comprehensive stainless steel mesh. Stainless steel perforated mesh. Stainless steel crimped wire mesh. Stainless steel chain link fence. Stainless steel expanded metal. Stainless steel welded wire mesh. Stainless steel hexagonal mesh. Stainless steel seat net. Stainless steel grill net. Stainless steel ore screen. Stainless steel tortoise shell mesh.